Effects of different surface conditioning methods on the bond strength of composite resin to amalgam.
Repairing amalgam restorations with composite resins using surface conditioning methods is a conservative treatment approach. This study investigated the effects of different conditioning methods that could be used for repair of amalgam fractures. Amalgam (N=96) was condensed into cavities within autopolymerizing polymethylmethacrylate (PMMA), and the exposed surface of each specimen (diameter, 6 mm; thickness, 2 mm) was ground finished. The specimens were randomly divided into nine experimental groups (n=12 per group), depending on the conditioning method used. The control group had natural central incisors with amalgam (n=12). The combination of the following conditioning methods was tested: silicacoating (Sc), sandblasting (Sb), metal primers, coupling agents, fiber (Fb) application, and opaquers (O). Five types of silanes, metal primers, or adhesives (Visiobond [V], Porcelain Photobond [PP], Alloy Primer [AP], Unibond sealer [Us], ESPE-Sil [ES]), and four opaquers, namely, Clearfil St Opaquer (CstO), Sinfony (S), Miris (M), and an experimental Opaquer (EO-Cavex), were used. The groups were as follows: group 1, Sc+ES+S+V; group 2, Sc+ES+CstO+V; group 3, Sc+ES+M+V; group 4, Sc+ES+EO+V; group 5, Sb+AP+S; group 6, Sb+AP+PP+CstO; group 7, Sc+ES+S+Fb+V+Fb; group 8-control, SC+ES+V; and group 9, Etch+Sc+ES+S+Us. One repair composite was used for all groups (Clearfil Photo Bond Posterior, Kuraray, Tokyo, Japan). Shear bond strengths (SBSs) (MPa ± SD) were evaluated after 5 weeks of water storage (analysis of variance [ANOVA], Tukey honestly significant differences [HSD], α=0.05). Group 1 exhibited significantly higher values (35.5 ± 4.1) than were seen in group 4 (19.4 ± 8.9), group 6 (19.1 ± 7.8), and group 8 (20.1 ± 4.1) (p<0.05). Surface conditioning techniques affected the bond strengths of composite adhesion to amalgam. Experimental opaquer exhibited lower values. Leaving a small border of enamel around the restoration decreased the bond strength.
Version: za2963e q8za4 q8zbc q8zc0 q8zd1 q8zef q8zfc q8zgd